Mixed-valent iron [Fe (II)-Fe (III)] minerals such as magnetite and green rust have received a
significant amount of attention over recent decades, especially in the environmental …

The corrosion evolution of a Mo–Cu-bearing fire-resistant steel in a simulated industrial
atmosphere was investigated by corrosion weight gain, XRD, EPMA, XPS, and polarization …

Abstract Effect of temperature and ultraviolet radiation (UV) on corrosion behavior of carbon
steel in high humidity atmospheric environment has been investigated by mass loss …

Corrosion and wear phenomenon has been responsible for the gradual deterioration of
components in industrial plants. This deterioration of components results in loss of plant …

The corrosion process of tinplate in 0.5 mol/L NaCl solution was investigated using the
electrochemical impedance spectroscopy (EIS), and the morphology and structure of the …

Sažetak Deep eutectic solvents (DESs) are a class of mixtures with melting points notably
lower than those of their raw constituent components. These liquids have found a …

The influence of Ni on the corrosion behavior of Ni‐containing weathering steel (Q415NH)
was investigated under alternate dry/wet conditions. The results suggested that the addition …

The corrosion resistance in saline conditions of weathering steel with different
concentrations of Si (1, 2 and 3wt.%) exposed to dip dry tests (simulating wet/dry cycles of …

Effects of chromium and manganese as alloying elements on corrosion resistance of carbon
steel were examined using evaluation of corrosion resistance in 60° C NaCl solution with a …

This work aimed to study the “blushing” phenomenon occurring on epoxy-phenolic coated
tinplate after boiling sterilization at 127℃ for 1 h. The corrosion resistance of the “blushing” …