The effect of Al addition on the corrosion behavior of high entropy alloys Al x CoCrFeNi (x=
0, 0.1, and 1.0) in supercritical water was investigated. The weight gain and oxide film …

The oxidation behavior of grain boundaries (GBs) was investigated on Alloy 690 after
exposure to simulated pressurized water reactor primary water. The tendency to form …

Internal oxidation was employed to determine oxygen permeability in the Fe-Ni system
between 1000 ºC and 1150 ºC at the oxygen partial pressures of Fe/FeO equilibrium. Fe-Ni …

This work aimed to analyze a failure that occurred on the TP347H reheater tube in a
supercritical circulating fluidized bed boiler from a thermal power plant. Optical microscopy …

The corrosion performance of the HR3C steels covered with salt deposition (Na 2 SO 4: K 2
SO 4= 1: 1) was investigated under various water vapor content at 700° C. Results show that …

The effects of steam on the oxidation behavior of model Al 2 O 3-scale forming Ni-base
alloys at 1000° C were studied. This was done by conducting tests using dry air and air+ …

The steam oxidation behavior of three heterogeneous HR3C alloys was investigated at 650°
C comparatively. After a long-term oxidation process for 1000 h, the results demonstrated …

Wagner's model of internal oxidation allows the prediction of an alloy's critical concentration
of oxide forming metal required to achieve a protective oxide scale at high temperatures …

Austenitic steels have been widely used as materials for super-heater and re-heater tubes of
fossil fuel power plants. 1, 2) Improvement of thermal efficiency is essential to save energy …

The cyclic oxidation behavior of TP347H ASS with different initial surface roughness at 800–
30° C was investigated. The R a of samples after 180#, 180#-400# SiC grinding was …