In this study, the potential of Fe3Al coating material as an environmentally friendly
alternative to coatings containing critical elements for brake discs was investigated. A buffer …

Oxidation, mixed oxidation–sulfidation and hot corrosion of ductile iron aluminide Fe3Al with
Cr addition have been examined at temperatures of 605° C and 800° C. It is observed that …

In the present study, a two-step surface treatment was employed to produce an iron-rich
aluminide surface layer on 9Cr1Mo steel. In the first step, the steel specimen was immersed …

Oxidation and sulfidation of Ni3Al has been studied in air and in 1% SO2/air gas mixture
atmosphere at 605, 800 and 1000° C. The experimental results show that Ni3Al appears to …

The isothermal high temperature corrosion behavior of an FeAl coating, coated on 9Cr1Mo
steel through laser surface alloying, was studied in atmospheres of pure oxygen and O 2+ …

!"#$%金属间化合物多孔材料的研究 Page 1 !"#$%金属间化合物多孔材料的研究 ! 邢毅!! 麻洪秋
况春江 (安泰科技股份有限公司,北京&’’’(&) 摘要: 采用粉末冶金方法制备了!"#$%多孔材料,研究 …

In this study, the potential of Fe3Al coating material as an environmentally friendly
alternative to coatings containing critical elements for brake discs was investigated. A buffer …

The application of thermal analysis in different fields of science and engineering is an
extensive topic which has been the subject of significant interest particularly since the …

Mechanical alloying process was studied in the Fe75Al25 system from elemental powders
using a dry tumbler ball mill. In the X-ray diffractions, the peaks of the Fe and the Al phases …

The pure Fe and pure Al (25 mol%) powder mixture was mechanically alloyed for various
times by a dry tumbler ball-milling. The magnetic property of the milled powder was …