The spontaneous passivation of (CoFeNi)(1-x)/3Crx alloys in sulfuric acid
The influence of at% Cr on the spontaneous passivation of (CoFeNi)(1-x)/3 Cr x alloys in 0.1
MH 2 SO 4 was investigated. During spontaneous passivation, Cr enrichment occurs due to …
MH 2 SO 4 was investigated. During spontaneous passivation, Cr enrichment occurs due to …
Microstructural complexity induced corrosion resistance in a novel compositionally complex alloy
The corrosion behavior of alloys is often compromised by microstructural complexity arise
from thermo-mechanical processing due to increased galvanic coupling susceptibility. Here …