[HTML][HTML] Restoration of Properties of Heat-Resistant Steel After Long-Term Operation in Steam Pipeline Bends of TPP by Heat Treatment
To improve the microstructure and mechanical properties of heat-resistant 12Kh1MF steel
after long-term operation in the stretched bend zone of the main steam pipeline of a thermal …
after long-term operation in the stretched bend zone of the main steam pipeline of a thermal …
Crack tip strain localisation on mechanics of fracture of heat resistant steel after hydrogenation
The fracture toughness of steel 15Kh2MFA (ІІ) after the PTL was investigated. It was
established that the crack start is a multilevel process, in which the defining role is played by …
established that the crack start is a multilevel process, in which the defining role is played by …
Development of a method for computer processing of fractographic images to assess the cohesion of inclusions to the matrix in the weld metal after its operational …
In this paper, the method for automated processing of digital fractographic SEM images
based on the modified local Otsu approach was developed. The effectiveness of the …
based on the modified local Otsu approach was developed. The effectiveness of the …
Digital analysis of shape and size of dimples of ductile tearing on fracture surface of long-operated steel
An improved dimple image quantitative analysis method based on mathematics morphology
was proposed. The developed method allows identifying the elements of the network of …
was proposed. The developed method allows identifying the elements of the network of …
Toughness and failure of heat resistant steel before and after hydrogenation
Fracture toughness of heat-resistant steel can be increased by a preliminary
thermomechanical loading called warm pre-stressing (WPS). The procedure creates a …
thermomechanical loading called warm pre-stressing (WPS). The procedure creates a …
Structural aspects of the degradation of the bend stretched zone
The structural features of heat-resistant steel 12Kh1MF after long-term operation in the
stretched zone of the bend main steam pipeline of the thermal power plant are analysed. It …
stretched zone of the bend main steam pipeline of the thermal power plant are analysed. It …
Estimation of the probability of fracture of the superheater collector of a thermal power plant
We study the influence of the depth of a surface defect and its shape factor on the probability
of fracture of a superheater collector made of 12Kh1MF steel after operation for 1.785· 10 5 …
of fracture of a superheater collector made of 12Kh1MF steel after operation for 1.785· 10 5 …
[PDF][PDF] Measurement of deformation hardening of heat-resistant steel of the WWER-type reactor
Presented investigations allowed revealing the correlation between microhardness and the
characteristics of strength of heat-resistant steel 15Kh2MFA (II). The sensitivity of the …
characteristics of strength of heat-resistant steel 15Kh2MFA (II). The sensitivity of the …
Hydrogen crack growth resistance of thermal power plant material collector
The influence of electrolytical hydrogenation on fracture toughness, corrosion crack-growth
resistance and fracture micromechanisms of operated 12Cr1MoV steel of thermal power …
resistance and fracture micromechanisms of operated 12Cr1MoV steel of thermal power …
[CITATION][C] Theoretical and Applie d Fracture Mechanics
P Yasniy, P Maruschak, R Bishchak, V Hlado… - 2009