Imaging and image-based fluid transport modeling at the pore scale in geological materials: A practical introduction to the current state-of-the-art
Fluid flow and mass transport in geological materials are crucial in diverse Earth science
applications. To fully understand the behavior of geological materials in this context, the …
applications. To fully understand the behavior of geological materials in this context, the …
Corrosion inhibition, inhibitor environments, and the role of machine learning
Machine learning (ML) is providing a new design paradigm for many areas of technology,
including corrosion inhibition. However, ML models require relatively large and diverse …
including corrosion inhibition. However, ML models require relatively large and diverse …
[HTML][HTML] Mitigation effects of over-aging (T73) induced intergranular corrosion on stress corrosion cracking of AA7075 aluminum alloy and behaviors of η phase grain …
The stress corrosion cracking (SCC) behaviors of over-aged and peak-aged AA7075
aluminum alloys in a 5 wt% NaCl solution were compared. Even though the over-aging …
aluminum alloys in a 5 wt% NaCl solution were compared. Even though the over-aging …
Observations of intergranular corrosion in AA2024-T351: The influence of grain stored energy
Aluminium alloy 2024-T351 was examined using a range of electron microscope techniques
at the early stages of attack after immersion in 0.1 M NaCl aqueous solution. At attack sites …
at the early stages of attack after immersion in 0.1 M NaCl aqueous solution. At attack sites …
Localized corrosion in AA2099-T83 aluminum–lithium alloy: The role of intermetallic particles
The corrosion behavior of intermetallic particles and their role in the process of localized
corrosion in AA2099-T83 aluminum–lithium alloy has been investigated. It was found that …
corrosion in AA2099-T83 aluminum–lithium alloy has been investigated. It was found that …
Cavitation erosion of the AA7050 aluminum alloy in 3.5 wt% NaCl solution—Part 1: mitigating effect by corrosion
Abstract The corrosion in 3.5 wt% NaCl solution caused a mitigated weight loss of the
aluminum alloy 7050 (AA7050) under cavitation erosion condition. The mechanism was …
aluminum alloy 7050 (AA7050) under cavitation erosion condition. The mechanism was …
Study of localized corrosion in AA2024 aluminium alloy using electron tomography
SEM based tomography of localized corrosion has been achieved using selective detection
of backscattered electrons. The high resolution tomography provides direct evidence that …
of backscattered electrons. The high resolution tomography provides direct evidence that …
Multiscale investigation of corrosion damage initiation and propagation in AA7075-T651 alloy using correlative microscopy
The evolution of the overall microstructure and contribution of constituent second phase
particles during the accelerated corrosion of AA 7075-T651 warrants further scrutiny. A …
particles during the accelerated corrosion of AA 7075-T651 warrants further scrutiny. A …
Intergranular corrosion in AA2024-T3 aluminium alloy: the influence of stored energy and prediction
X Zhang, Y Jiao, Y Yu, B Liu, T Hashimoto, H Liu… - Corrosion …, 2019 - Elsevier
In the present work, microstructure and intergranular corrosion behaviour of AA2024-T3
alloy are studied. Using electron diffraction techniques to correlate stored energy distribution …
alloy are studied. Using electron diffraction techniques to correlate stored energy distribution …
The effect of artificial ageing heat treatments on the corrosion-induced hydrogen embrittlement of 2024 (Al–Cu) aluminium alloy
This work is focused on the role of microstructure (S-type particles) that are precipitated in
the aluminium matrix due to artificial ageing on the tensile ductility decrease of 2024 …
the aluminium matrix due to artificial ageing on the tensile ductility decrease of 2024 …