Monodispersed Fe3O4 nanoparticles of size∼ 10 nm were processed by a simple ultrasonic
assisted co-precipitation method, mechanically mixed with graphene oxide, and thermally …

A 3 wt% La-promoted Ni/Al 2 O 3 catalyst was prepared via wet co-impregnation technique
and physicochemically-characterized. Lanthanum was responsible for better metal …

Indium oxide nanoparticles of∼ 12 nm were synthesized by a simple chemical route using
indium (III) nitrate. Nanoparticles are formed after calcining the dried precursor in air at 400° …

Nanostructured Fe3O4 nanoparticles were prepared by a simple sonication assisted co-
precipitation method. Transmission electron microscopy, X-ray diffraction and BET surface …

Pure LaAlO3 powder was prepared by a combustion synthesis processing using a
concentrated solution of nitrates of lanthanum and aluminate as oxidiser, and glycine acid …

Rare earth nanomaterials with nanometer to submicronmeter crystalline sizes are an
important class of materials displaying interesting physical and chemical properties …

The effect of oxygen diffusion on the thermal decomposition kinetics of La [Fe (CN) 6]· 5H 2
O has been explored. In particular, the critical conditions under which LaFeO 3 can be …

This letter describes the synthesis of CaAl12O19 powders using micro reactors made of
Igepal CO520/water/cyclohexane microemulsions. Characterization of the powder was done …

Spherical LaAlO3 nanoparticles in a reverse microemulsion consisting of solution (water
phase), Tween-80 and Span-80 (surfactant), n-butanol (cosurfactant, and cyclohexane (oil …

Nanocrystalline lanthanum monoaluminate (LaAlO3) powders were prepared by chemical
coprecipitation using 25vol.% of NH4OH, 0.05 M La (NO3) 3· 6H2O and 0.05 M Al (NO3) 3 …